Corrosion resistance assessment of nickel-titanium endodontic files with and without heat treatment.

OBJECTIVES: The aim of this study was to evaluate the corrosion resistance of heat-treated (Reciproc and WaveOne) and non-heat-treated (ProTaper and Mtwo) superelastic nickel-titanium endodontic files when immersed in a 5.25% sodium hypochlorite solution. MATERIALS AND METHODS: Anodic polarization curves were obtained with potential sweeps that began at the open circuit potential or corrosion potential (Ecorr). The pitting potential (Epit) was identified on the anodic polarization curve as the potential at which a sudden increase in current was observed. The micromorphology of the 28 tested files was analyzed before and after the electrochemical assay using scanning electron microscope (SEM). The data were analyzed using 1-way analysis of variance with the post hoc Bonferroni test (for Ecorr) and the Student t-test for independent samples (for Epit). RESULTS: The mean Ecorr values were 0.506 V for ProTaper, 0.348 V for Mtwo, 0.542 V for Reciproc, and 0.321 V for WaveOne files. Only WaveOne and Protaper files exhibited pitting corrosion, with Epit values of 0.879 V and 0.904 V, respectively. On the SEM images of the ProTaper and WaveOne files, cavities suggestive of pitting corrosion were detected. CONCLUSIONS: Signs of corrosion were observed in both heat-treated and non-heat-treated files. Of the evaluated files, WaveOne (a heat-treated file) and ProTaper (a non-heat-treated file) exhibited the lowest corrosion resistance.

Caracterização química e metalográfica dos aços inoxidáveis de implantes removidos de pacientes / Chemical and metallographic characterization of stainless steel in implants removed from patients

OBJETIVO: Este trabalho estudou a composição química e metalográfica (microestrutura, tamanho de grão, teor de inclusões) de aços inoxidáveis austeníticos, desenvolvidos para aplicações como biomateriais, utilizados na fabricação de implantes ortopédicos. MÉTODO: Foram analisados doze implantes removidos de pacientes afetados por quadro inflamatório. As análises químicas foram desenvolvidas pelas técnicas Espectrometria de Emissão Ótica e Microanálise por Dispersão de Energia (EDS) e o tamanho de grão foi determinado por microscopia ótica e Microscopia Eletrônica de Varredura (MEV) conforme norma ASTM E 1382 97. RESULTADOS: Observou-se que, todos os implantes apresentavam tamanho de grão superior ao recomendado pela norma, constatou-se também a presença de ferrita delta em dez dos doze implantes removidos, que de acordo com a norma ASTM F138-92 não deveriam ser percebidas microscopicamente com um aumento de 100 vezes. CONCLUSÕES: Em oito casos existe forte indicação de que as inflamações foram desencadeadas pela corrosão por pite. Nivel de Evidência III, Revisão sistemática de Estudos .

OBJECTIVE: This study examines the chemical and metallographic composition (microstructure, grain size, inclusion content) of austenitic stainless steel developed as biomaterials for used in the manufacture of orthopedic implants. METHOD: An analysis was carried out of twelve implants removed from patients affected by inflammation. Chemical analyses were carried out using Optical Emission Spectrometry and Energy Dispersive Microanalysis (EDS), and the grain size was determined by optical microscopy and scanning electron microscopy (SEM) according to ASTM Standard E 1382 97. RESULTS: It was observed that all the implants had a larger grain size than is recommended by the Standard. The presence of delta ferrite was also observed in ten of the twelve implants removed, which according to ASTM Standard F138-92, should not be perceived microscopically under magnification of 100x. CONCLUSIONS: In eight cases, there is a strong indication that the inflammation was triggered by pitting corrosion. Level of Evidence: Level III, Systematic review of studies.

Ligas para amálgama contendo zinco: quando devemos usá-las? / Dental amalgam alloy containing zinc: when should we use them?

O presente estudo teve por objetivo avaliar, por revisäo da literatura, o efeito da inclusäo do zinco nas ligas de amálgama dentário. Para isso, foram analisadas a microestrutura, as propriedades físicas, a corrosäo, a deterioraçäo, fraturas marginais e a citoxicidade do amálgama

Estabilidade dimensional das siliconas por condensação / Dimensional stability of the condensation silicone

Dentre os materiais de moldagem elastoméricos, a silicona, por reação de condensação, se destaca como a de maior utilização no Brasil (cerca de 78 por cento). Apesar de apresentar uma série de propriedades físicas vantajosas como a flexibilidade adequada, boa recuperação elástica, sabor e odor agradáveis e satisfatório tempo de presa, a silicona por reação de condensação possui elevada contração linear de duas a quatro vezes superior a dos demais elastômeros e, especialmente, da volatilização de álcool etílico durante a reação de polimerização. Considerando que a volatilização desse subproduto é a razão direta da pressão exercida pela temperatura, os autores se propuseram a desenvolver metodologia que objetivasse melhorar essa propriedade com base na variação da temperatura. Os resultados permitiram verificar que à temperatura ambiente houve grande contração, especialmente com a marca Optosil-Kulzer (0,411 por cento em 24h e 0,753 por cento em cinco dias). Entretanto, à baixa temperatura, houve significativa diminuição da alteração dimensional dessa marca e estabilidade com a marca Speedex-Coltène